AN104 – Thermophysical properties of the composite ceramic-salt system (SiO2/Na2SO4)

REFERENCE

Thermophysical properties of the composite ceramic-salt system (SiO2/Na2SO4)   W. Notter, Th. Lechner, U. Gross and E. Hahne Thermochimica Acta, 218 (1993) 455-463.

INTRODUCTION

A composite ceramic-salt packed bed configuration is being developed for high-temperature thermal storage. The thermophysical properties of the more particular hybrid system SiO2/ Na2SO4 have been investigated in the range from room temperature above the melting point of the salt, 884°C. The Na2SO4 fraction in the composite materials was varied between 20 and 50%. The following properties were measured: specific enthalpy, coefficient of thermal expansion and thermal diffusivity.

AN-104

EXPERIMENTAL

The specific enthalpy of the above mentioned composite materials was measured with a drop calorimeter.
A sample (a cylinder of 5 mm in diameter and 5 mm long) tempered at room temperature is dropped into a heated measuring crucible which is completely enclosed by a thermoelectric pile. During the heating up of the sample the resulting heat flow is measured by the thermopile. The enthalpy difference between room temperature and the final sample temperature is determined by an integration of the measured heat flow. The measurements were carried out in an atmosphere of slowly flowing argon. The device has been checked with pure MgO.

RESULTS

The examined samples consist of mixtures of 20/80, 40/60 and 50/50 wt% Na2SO4 and different modifications of SiO2.
The use of a drop calorimeter allows the determination of the absolute value of the specific enthalpy and the enthalpy change on transitions very exactly.
Fig. 1a shows measured specific enthalpy values of Na2SO4, the cristobalite and the quartz phase of SiO2 and of a 50/50-sample. The measured values above and below the melting point are interpolated linearly.
An examination of the calorimetric measurements shows that a simple weight fraction mixture rule can be applied, which is reasonable since chemical reactions between SiO2 and Na2SO4 are not expected. Assuming the cristobalite fraction to be 80 % of the ceramic matrix material, calculated enthalpy values fit the measurements of 20/80, 40/60 and 50/50 samples shown in Fig. 1b within the scatter of the data.